HOLDING TIME PADA SIFAT FISIK PENGELASAN SMAW BAJA ASTM-A36 MELALUI UJI PENETRAN
DOI:
https://doi.org/10.31599/khc2jj97Keywords:
ASTM A36, Holding Time, Penetrant TestAbstract
In the industrialized world, low-carbon steel was often used as a construction material. One of the problems obtained in the low carbon steel welding process was its nature susceptible to shakes. The minimize the formation of residual voltage in the connection area (Heat Affected Zone) can be done by the Post Weld Heat Treatment (PWHT) process The purpose of this study was to find out the effect caused by variations in heat treatment on heating steel ASTM A36 (Holding Time) to penetrant tests and determine the suitable temperature given to ASTM A36 steel after the welding process. The PWHT process was carried out with several variations of Holding Time, namely 1 hour, 2 hours, and 3 hours at 400 °C. Based on penetrant testing showed that the best value in Holding Time was 3 hours with no appearance of porosity defects
Downloads
References
Amstead, B.H., F. Philip, O., dan Myron, L.B., (1979). Ted J.Arismunandar Wiranto (Penterjemah) Jakarta, Teknologi Mekanik, Edisi Ketujuh Jilid 1. Erlangga: Jakarta.
Anggigi, H., Budiarto, U., dan Zakki, A.F., (2019). Analisa Pengaruh Temperatur Normalizing pada Sambungan LAS SMAW (Shielded Metal Arc Welding) Terhadap Kekuatan Tarik, Tekuk dan Mikrografi Baja Karbon Rendah. Jurnal Teknik Perkapalan, Vol. 7, No. 4, pp. 04-513.
Bangsawan, I.G., Suharno, dan Harijanto, B., (2012). Pengaruh Variasi Temperatur Holding Time Dengan Media Quenching Oli Mesran SAE 40 Terhadap Struktur Mikro dan Kekerasan Baja ASSAB 760, Nozzel Jurnal Pendidikan Teknik Mesin, Vol. 1, No. 2, pp. 1-13.
Marwanto, A, dan Ardian, A., (2005). Pengembangan Bahan Ajar Mata Kuliah Metalurgi Las Melalui Penelitian Pengaruh Bentuk Kampuh Pada Pengelasan SMAW Baja Eyser Terhadap Sifat Mekanik, Jurnal Dinamika, Vol. 3, No. 1.
Fauzan, H., (2015). Pengaruh Tekanan Dan Lama Plasma Nitriding Terhadap Kekerasan Dan Laju Korosi Baja Tahan Karat AISI 410, Fakultas Teknik Universitas Gadjah Mada, Yogyakarta.
Prasetyo. E.B., (2019). Analisis Media Pendinginan PWHT Pada Pengelasan Aluminium 6061 Dengan Proses GTAW Terhadap Pembuatan Kurva DAC Dan Nilai Kekerasan. Surabaya: Politeknik Perkapalan Negeri Surabaya.
Pratama, R.Y, Basuki, M. dan Pranatal, E., (2020). Pengaruh Variasi Arus Pengelasan SMAW Untuk Posisi Pengalasan 1G Pada Material Baja Kapal SS 400 Terhadap Cacat Pengelasan. Prosiding Seminar Teknologi Kebumian dan Kelautan: Institut Teknologi Adhi Tama Surabaya, Vol. 2, No. 1.
Surdia, T, dan Chijiwa, K., (2017). Kajian Distribusi Kekerasan dan Perubahan Struktur Mikro Pada Proses Quenching Terhadap Variasi Diameter Dalam Baja Karbon Sedang Tipe SAE 10-40. Jurnal Ilmiah, Teknik Mesin ITM, Vol. 3, No. 2.
Wijoyo dan Indriyanto, B., (2016). Pengaruh Masukan Panas (Heat Input) Terhadap Ketangguhan Impak Sambungan Las TIG A1-13,5Si, Jurnal Simetris, Vol. 7, No. 2.
Wirarchi, D., Mulyadi, Y. dan Supomo, H., (2010). Analisa Pengaruh Multiple Repair Welding Pada Material Properties Weld Joint Material Pipa ASTM A106 GR.B SCH 80, Jurnal Tugas Akhir, Teknik Kelautan, ITS - Surabaya